Fe-Cr-Al alloy Electric Heating Resistance Wire
Description
Fe-Cr-Al alloy wires are made of iron chromium aluminum base alloys containing small amounts of reactive elements such as yttrium and zirconium and produced by smelting, steel rolling, forging, annealing, drawing, surface treatment, resistance control test, etc.
The high aluminum content, in combination with the high chromium content let the scaling temperature can reach to 1425ºC (2600ºF);
Fe-Cr-Al wire was shaped by means of high speed automatic cooling machine of which the power capacity is controlled by computer, they are available as wire and ribbon(strip).
Product forms and size range
Round wire
0.010-12 mm (0.00039-0.472 inch) other sizes are available on request.
Ribbon (flat wire)
Thickness: 0.023-0.8 mm (0.0009-0.031 inch)
Width: 0.038-4 mm (0.0015-0.157 inch)
Width/thickness ratio max 60, depending on alloy and tolerance
Other sizes are available on request.
Resistance electric heating wire has strong antioxidant properties, but a variety of gases in furnaces such as air, carbon, sulfur, hydrogen and nitrogen atmosphere, still have a certain impact on it.
Although these heating wires all have had antioxidant treatment, the transportation, winding, installation and other process will cause damage to a certain extent and reduce its service life.
In order to extend the service life, customers need to do pre oxidation treatment before using. The method is to heat alloy elements which have installed completely in the dry air to the temperature (lower 100-200C than its maximum using temperature), heat preservation for 5 to 10 hours, then cooling slowly with furnace.