Kanth-al LT heating wire resistance wire ferritic iron­chromium­aluminium FeCrAl alloy

Short Description:


  • model name: Kanthal LT,0Cr19Al3
  • material: Ferro Chrome Aluminium
  • conductor type: solid
  • surface: bright
  • trademark: TANKII
  • Product Detail

    FAQ

    Product Tags

    Product Description

    furnace fecral resistance heating wire

    Fe-Cr-Al Alloy
    Longer high temperature service life
    Superior oxidation resistance
    Higher rresistance

    Specification

    High quality Low Price FeCrAl Alloy Wire

     

    Fe-Cr-Al alloy has the characteristic of high resistivity,low temperature resistance coefficient,high operating temperature,good anti-oxidation and anti-corrosion under high temperature.

     

    It is widely used in industrial furnace, household appliances, industry furnace, metallurgy, machinery, aircraft, automotive, military and other industries producing heating elements and resistance elements.

     

    nichrome heating alloy includes pure nickel, NiCr alloy, Fe-Cr-Al alloy and copper nickel alloy.

     

    FeCrAl resistance wire grade: 0Cr25Al5, 1Cr13Al4, 0Cr23Al5, 0Cr27Al7Mo2, 0Cr21Al6Nb, 0Cr21Al4, 0Cr21Al6.

     

    In the form of wire, ribbon and strip, one kind of material Fe-Cr-Al alloy.

     

    Wire: 0.018mm-10mm

    Rod: 8mm-50mm

    Ribbon: 0.05*0.2mm-2.0*6.0mm
    Strip: 0.5*5.0mm-5.0*250mm

     

    Alloy Nomenclature Performance 1Cr13Al4 0Cr25Al5 0Cr21Al6 0Cr23Al5 0Cr19Al3 0Cr21Al6Nb 0Cr27Al7Mo2
    Chemical Compostion (%) Cr 12.0-15.0 23.0-26.0 19.0-22.0 20.5-23.5 18.0-21.0 21.0-23.0 26.5-27.8
    Al 4.0-6.0 4.5-6.5 5.0-7.0 4.2-5.3 3.0-4.2 5.0-7.0 6.0-7.0
    Re opportune opportune opportune opportune opportune opportune opportune
    Fe Rest Rest Rest Rest Rest Rest Rest
    Nb0.5 Mo1.8-2.2
    Max. continuous service temp. of element(%) 950 1250 1250 1250 1100 1350 1400
    Resistivity at 20℃(μΩ*m) 1.25 1.42 1.42 1.35 1.23 1.45 1.53
    Density(g/cm3) 7.4 7.1 7.16 7.25 7.35 7.1 7.1
    Thermal conductivity(KJ/m*h*℃) 52.7 46.1 63.2 60.2 46.9 46.1
    Coefficient of lines expansion(α*10-6/℃) 15.4 16 14.7 15 13.5 16 16
    Melting point approx.(℃) 1450 1500 1500 1500 1500 1510 1520
    Tensile strength(N/mm2) 580-680 630-780 630-780 630-780 600-700 650-800 680-830
    Elongation at rupture(%) >16 >12 >12 >12 >12 >12 >10
    Variation of area(%) 65-75 60-75 65-75 65-75 65-75 65-75 65-75
    Repeat Bending frequency(F/R) >5 >5 >5 >5 >5 >5 >5
    Hardness(H.B.) 200-260 200-260 200-260 200-260 200-260 200-260 200-260
    continuous service time(Hours/℃) ≥80/1300 ≥80/1300 ≥80/1300 ≥80/1250 ≥50/1350 ≥50/1350
    Micrographic structure Ferrite Ferrite Ferrite Ferrite Ferrite Ferrite Ferrite
    Magnetic properties Magnetic Magnetic Magnetic Magnetic Magnetic Magnetic Magnetic

     